- DuPont Elvaloy® 2615 AC Ethylene and 15% Ethyl Acrylate Copolymer
DuPont Elvaloy® 2615 AC Ethylene and 15% Ethyl Acrylate Copolymer
| Category | Polymer , Film , Thermoplastic |
| Manufacturer | DuPont Packaging and Industrial Polymers |
| Trade Name | Elvaloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvaloy® 2615 AC Ethylene and 15% Ethyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Because of its high flexibility and high filler loading capacity, Elvaloy® 2615 AC is particularly suited for injection molded parts in the automotive and furniture industries. It also offers excellent adhesion properties to various substrates and has very good heat stability, making is suitable in extrusion coating and lamination applications.Elvaloy® 2615 AC has a wide processing latitude in molding and extrusion equipment. It has good flow characteristics and lower melting range than low density polyethylene.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 - ISO 1183 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 88 | 88 | ASTM D2240 - ISO 868 |
| Hardness, Shore D | 31 | 31 | ASTM D2240 - ISO 868 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| Elongation at Break | 740 % | 740 % | 500 mm/min; ASTM D638 - ISO 527-2 |
| Tensile Modulus | 0.0400 GPa | 5.80 ksi | 1 mm/min; ASTM D638 - ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 97.0 °C | 207 °F | By DSC; ASTM D3418 - ISO 3146 |
| Vicat Softening Point | 58.0 °C | 136 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 °C | 302 °F | Extrusion lamination and extrusion coating |
| 150 °C | 302 °F | Cast film | |
| 150 °C | 302 °F | Blown film | |
| Middle Barrel Temperature | 160 °C | 320 °F | Blown film |
| 210 °C | 410 °F | Cast film | |
| 220 °C | 428 °F | Extrusion lamination | |
| Front Barrel Temperature | 170 °C | 338 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Adapter Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast Film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Die Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination |
| Descriptive Properties | Value | Comments |
|---|---|---|
| EA-Content | 15 wt.% | DuPont Method |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HP2JP PC (Asia Pacific)
- ExxonMobil LD 513.48 Molding, Extrusion and Compounding Resin (discontinued **)
- ITW Devcon Rubber Repair / Castable Urethane High Temp Edge & Seal (T-36), Amber
- Gwent Electronic Materials P2121112P14 Nitrogen Plasma Modified Single and Double Walled Carbon Nanotubes
- Solvay Specialty Polymers FOMBLIN® Y L-VAC 06/6 PFPE Pump Oil
- Unipetrol PP MONSTEN® MT 812 Polypropylene Random Copolymer
- BASF Ecovio® C2332 F Blend Biodegradable Polyester
- Chang Chun Plastic PBT4830 Fire Retardant & 30% Glass Fiber Enforced Grade PBT
- Techmer Lehvoss Compounds Luvotech™ J-4/35 BK223 PA6/12 (discontinued **)
- Spartech PP7240 Calcium Carbonate Filled High Impact Copolymer
Copyright © lookpolymers.com All Rights Reserved