Eurostar Starflam PX06009 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PX06009 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PX06009 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.0090 cm/cm @Thickness 4.00 mm |
0.0080 - 0.0090 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| Elongation at Break | >= 3.2 % | >= 3.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.20 GPa | 899 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.20 GPa | 899 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.20 kJ/m² | 1.52 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 95.0 kJ/m² | 45.2 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| UL RTI, Mechanical with Impact | 125 °C | 257 °F | |
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ HC 2185G Polyvinyl Chloride, Flexible (PVC, Flexible)
- Ineos TUB 172 HDPE
- LATI Latamid 6 H2 G/30-V2HF PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- A. Schulman POLYBATCH™ XAMF-500-T Process Aid Concentrate, Concentrate Based In LLDPE
- DuPont™ Bynel® 30E753 Anhydride Modified Ethylene Vinyl Acetate
- China-Yixing Longly Refractories ASM-125 Cordierite-Mullite
- Eurotec® Tecopet® PT70 GR30 NL100 XA20 PET, 30% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- Bhansali Engineering Abstron KU600N ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved