Hexcel® HexTOOL™ M61 Quasi-isotropic High Temperature Prepreg Tooling Compound

Category	Other Engineering Material , Polymer , Thermoset , Epoxy
Manufacturer	Hexcel
Trade Name	HexTOOL™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Hexcel® HexTOOL™ M61 Quasi-isotropic High Temperature Prepreg Tooling Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HexTOOL™ Tooling Compound is randomly layered strips of uni-directional prepreg which is consolidated into rolled goods. It can be utilized as multi-ply quasi-isotropic hand lay-up, and subsequently CNC milled to close tolerance. HexTOOL™ has proved to be dimensionally stable with the ability to hold vacuum integrity before and after machining, and after more than 500 part cure cycles. Fabricated from Hexcel's BMI resin HexPly® M61, HexTOOL™ tools are ideally suited for 356°F (180°C) cure carbon fiber tools. This makes them lighter weight, more energy efficient than tools made of steel or Invar®, and more cost-effective with tighter mold tolerance than standard composites.Information provided by Hexcel

Physical Properties	Metric	English	Comments
Thickness	32.3 microns	1.27 mil	Cured Ply Thickness: HexTOOL™ M61 (2000); Based on nominal prepreg properties
	64.5 microns	2.54 mil	Cured Ply Thickness: HexTOOL™ M61 (4000); Based on nominal prepreg properties

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	210 MPa @Temperature 180 °C	30500 psi @Temperature 356 °F	Dry; EN2561
	260 MPa @Temperature 23.0 °C	37700 psi @Temperature 73.4 °F	Dry; EN2561
Tensile Modulus	40.0 GPa @Temperature 180 °C	5800 ksi @Temperature 356 °F	Dry; EN2561
	41.0 GPa @Temperature 23.0 °C	5950 ksi @Temperature 73.4 °F	Dry; EN2561
Flexural Strength	380 MPa @Temperature 23.0 °C	55100 psi @Temperature 73.4 °F	Dry; EN2562
Flexural Modulus	38.0 GPa @Temperature 23.0 °C	5510 ksi @Temperature 73.4 °F	Dry; EN2562
Compressive Strength	270 MPa @Temperature 180 °C	39200 psi @Temperature 356 °F	Dry; EN2850B
	300 MPa @Temperature 23.0 °C	43500 psi @Temperature 73.4 °F	Dry; EN2850B
Compressive Modulus	30.0 GPa @Temperature 180 °C	4350 ksi @Temperature 356 °F	Dry; EN2850B
	32.0 GPa @Temperature 23.0 °C	4640 ksi @Temperature 73.4 °F	Dry; EN2850B
Shear Strength	43.0 MPa @Temperature 180 °C	6240 psi @Temperature 356 °F	Short Beam Shear, Dry; EN2563
	50.0 MPa @Temperature 23.0 °C	7250 psi @Temperature 73.4 °F	Short Beam Shear, Dry; EN2563

Thermal Properties	Metric	English	Comments
CTE, linear	4.00 µm/m-°C	2.22 µin/in-°F	In Plane; ASTM E289-95
Maximum Service Temperature, Air	218 °C	424 °F
Glass Transition Temp, Tg	275 °C	527 °F	Postcured, Dry

Processing Properties	Metric	English	Comments
Shelf Life	12.0 Month @Temperature -18.0 °C	12.0 Month @Temperature -0.400 °F

Descriptive Properties	Value	Comments
Autoclave Work Life (Days)	20	At 21°C
Minimum Initial Cure Temperature (°C)	190
Nominal Ply Areal Weight (g/m2)	2000
	4000
Nominal Resin Content (%)	38	By weight