Fiberfil® J-60/20/E4 Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-60/20/E4 Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0040 cm/cm @Thickness 6.35 mm |
0.0040 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 - 110 | 100 - 110 | ASTM D785 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Yield | 3.5 % | 3.5 % | ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm |
1.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 6900 BLK
- Resinlab® CYNERGY CA6907 Adhesive
- RheTech Products T40P108-01A 40% Talc Reinforced Polypropylene, Black
- Mytex Polymers AS88LW-01 Polypropylene, Compounded, Elastomer
- Indium Corp. Indalloy 130 Tin-Lead Solder Alloy
- DSM Akulon® S223-GM35 (Dry) 15% Glass Reinforced, 25% Mineral Reinforced Nylon 66 (North America)
- Dow AFFINITY™ PF 1140 Polyolefin Plastomer
- Braskem INSPIRE™ 404 Performance Polypropylene Polymer
- Adell ZR-17 33% Glass Reinforced Nylon/Olefin Alloy
- SABIC Innovative Plastics LNP LUBRICOMP DL002 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved