Eurostar Starflam P10002Z PA6, Flame Retardant, Extrusion
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam P10002Z PA6, Flame Retardant, Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam P10002Z is an Unfilled, Halogen Free, Red Phosphorous Free, Flame Retardant, Polyamide 6 Extrusion ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 4.00 mm |
0.010 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 5.6 % | 5.6 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.7 % | 3.7 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.10 GPa | 450 ksi | 2 mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
41.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Oxygen Index | 32 % | 32 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 0.750 mm |
1760 °F @Thickness 0.0295 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 245 °C | 455 - 473 °F | |
| Zone 3 | 240 - 260 °C | 464 - 500 °F | |
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 3200-25 Fiberglass Reinforced SMC
- DuPont Performance Polymers Zytel® 73G30T NC010 Nylon 6 (Unverified Data**)
- Solvay TECHNYL® A 216 V15 Black 21N PA66, 15% glass fiber, Conditioned
- A. Schulman PP 3491 Polypropylene Homopolymer Polypropylene
- Arlon 55609R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Scotch-Weld™ DP600 Concrete Repair and Self-Leveling
- 3M FM049 Clear Polyester Label Product
- Overview of materials for Linear Medium Density Polyethylene (LMDPE), Rotational Molded
- LG Chemical HYPERIER IP1106 PA-PE Nanoclay Compound
- PolyOne Syncure™ System S117FH Polyethylene, Crosslinked (XLPE)
Copyright © lookpolymers.com All Rights Reserved