Ineos Nova Styrosun® 3600 Weather Resistant High Impact Styrenic Polymer
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Nova |
| Trade Name | Styrosun® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova Styrosun® 3600 Weather Resistant High Impact Styrenic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Outdoor weatherablePhysical property retention after UV exposurePaintable and printableExcellent toughness Can be injection molded or co-extruded Easy to process, no drying required Applications: Inset window frames on doors Outdoor signsIrrigation/sprinkler systemsGardening and yard accessoriesRecreational vehicle componentsInformation provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.Â
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 5.3 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.3 g/10 min @Load 11.0 lb, Temperature 392 °F |
old Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Tensile Modulus | 2.16 GPa | 313 ksi | ASTM D638 |
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Flexural Modulus | 2.04 GPa | 296 ksi | ASTM D790 |
| Izod Impact, Notched | 2.00 J/cm | 3.75 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | annealed; ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 204 °C | 360 - 399 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 399 - 441 °F | |
| Front Barrel Temperature | 216 - 238 °C | 421 - 460 °F | |
| Melt Temperature | 221 - 243 °C | 430 - 469 °F | |
| Mold Temperature | 32.0 - 54.0 °C | 89.6 - 129 °F | |
| Back Pressure | 0.345 MPa | 50.0 psi |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 H-TF20 Nylon 6 for injection molding, 20% PTFE lubricated
- Polykemi AB POLYfill PPH GF5010 VT2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Heat Resistant
- SABIC Innovative Plastics LNP THERMOCOMP PFW64 PA 6
- Teknor Apex TEKBOND® 6700-65 Thermoplastic Elastomer
- DuPont Conpol™ 5B10S1 Ethylene-Methacrylic Acid Additive Resin
- ExxonMobil Isopar™ J Isoparaffin Fluid
- 3M FVT30E Tire Label Product
- Beijing Ranger Chem BLUESTAR® 1135 PBT
- Arlon 44571XB015 0.015" Uncured Silicone Rubber with Fiberglass Substrate
- DuPont Performance Polymers Zytel® 80G14A NC010A Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved