Eurostar Starflam BFR460A PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam BFR460A PA6, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam BFR460A is a Flame Retardant, Glass Fiber Reinforced Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -40.0 °C |
2.86 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
9.44 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 105 µm/m-°C @Temperature 23.0 - 60.0 °C |
58.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| UL RTI, Electrical | 65.0 °C | 149 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Supradel® HTS-2420 High Temperature Sulfone Resin (discontinued **)
- Kraton® D1192 A (SBS) Liner Block Copolymer
- Lavergne VYPET VNT 615 HP PET 15% Glass Reinforced
- Solvay Specialty Polymers Tecnoflon® T 636/L Fluoroelastomer
- A. Schulman POLYFORT™ PP 3701
- A. Schulman POLYBATCH™ Dark Grey LL80362/4 Concentrate Based In LLDPE
- A. Schulman PP 1901-01 Polypropylene High-Flow Homopolymer Polypropylene
- Eurostar Staramide P1000J5 PA6, Impact Modified, Injection Molded
- Eurostar Staramide PF007 PA6, 35% Glass Fiber Filled, Injection Molded
- Solvay RHODAFAC® RS-610/A25 Surfactant
Copyright © lookpolymers.com All Rights Reserved