Eurostar Starflam AFR200B PA66, Flame Retardant, Injection Molding

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam AFR200B PA66, Flame Retardant, Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide AFR200B is an Unfilled, Flame Retardant Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
Water Absorption at Saturation 6.5 %

@Temperature 23.0 °C
 6.5 %

@Temperature 73.4 °F
 ISO 62-1
Linear Mold Shrinkage, Flow 0.010 - 0.015 cm/cm
0.010 - 0.015 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ISO 2039-2
Tensile Strength at Break 80.0 MPa
11600 psi
50 mm/min; ISO 527
Tensile Strength, Yield 80.0 MPa
11600 psi
50 mm/min; ISO 527
Elongation at Break 6.0 %
6.0 %
50 mm/min; ISO 527
Elongation at Yield 3.7 %
3.7 %
50 mm/min; ISO 527
Tensile Modulus 3.00 GPa
435 ksi
1 mm/min; ISO 527
Flexural Strength 105 MPa
15200 psi
2 mm/min; ISO 178
Flexural Modulus 2.80 GPa
406 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature -40.0 °C
 1.43 ft-lb/in²

@Temperature -40.0 °F
 80x10x4; ISO 180/1A
4.00 kJ/m²

@Temperature -20.0 °C
 1.90 ft-lb/in²

@Temperature -4.00 °F
 80x10x4; ISO 180/1A
5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80x10x4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 85.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 47.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 85.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 47.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Hot Ball Pressure Test 123 - 127 °C
253 - 261 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
421 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 245 °C
473 °F
B/120; ISO 306
UL RTI, Electrical 65.0 °C
149 °F
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL RTI, Mechanical without Impact 65.0 °C
149 °F
Flammability, UL94 V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 29 %
29 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Comparative Tracking Index 250 V
250 V
M; IEC 60112
350 V
350 V
IEC 60112
Processing Properties Metric English Comments
Zone 1 260 - 270 °C
500 - 518 °F
Zone 2 270 - 280 °C
518 - 536 °F
Zone 3 270 - 280 °C
518 - 536 °F
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
 167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %