Eurostar Staramide BK8 PA6, 40% Mineral Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide BK8 PA6, 40% Mineral Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide BK8 is a 40% Mineral Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 112 | 112 | ISO 2039-2 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.80 GPa | 841 ksi | 1 mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -20.0 °C |
2.38 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -40.0 °C |
2.38 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A | |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 230 °C | 446 °F | B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |
| Zone 3 | 240 - 270 °C | 464 - 518 °F | |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- LATI LATISTAT 43/7-02 Low Density Polyethylene (LDPE) Base Conductive Plastic (discontinued **)
- LG Chemical Lupox® GP2056F PBT+GF5%
- Mitsui UNISTOLEâ„¢ R-100S1 Polyolefinic Primer/ Adhesive
- Fainplast Compounds GS 7325 Flexible PVC, Injection Molding for Technical Items
- Dow Corning EG-3000 THIXOTROPIC GEL PARTS A&B
- BASF Ultramid® A3W PA66 (Conditioned)
- Arlon T2030-R004-12 0.030" Cured Self-Fusing Silicone Rubber Tape
- Beijing Evergrow Resources PTFE, 20% Glass Fiber Filled
- Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Conditioned (discontinued **)
Copyright © lookpolymers.com All Rights Reserved