Eurostar Staramide BG7H PA6, 35% Glass Fiber Filled, Heat Stabilized, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide BG7H PA6, 35% Glass Fiber Filled, Heat Stabilized, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide BG7H is a Heat Stabilized, 35% Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.60 % @Temperature 23.0 °C |
1.60 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 6.2 % @Temperature 23.0 °C |
6.2 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0035 cm/cm | 0.0015 - 0.0035 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 112 | 112 | ISO 2039-2 |
| Tensile Strength at Break | 180 MPa | 26100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 280 MPa | 40600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.75 GPa | 1410 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A | |
| 12.0 kJ/m² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
11.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
45.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 216 °C | 421 °F | B/120; ISO 306 |
| 217 °C | 423 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| Flame Spread | 5.00 mm/min @Thickness 3.00 mm |
0.197 in/min @Thickness 0.118 in |
FMVSS Burning Speed |
| 10.0 mm/min @Thickness 2.00 mm |
0.394 in/min @Thickness 0.0787 in |
FMVSS Burning Speed | |
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.6 @Frequency 50.0 - 60.0 Hz |
3.6 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0065 @Frequency 50.0 - 60.0 Hz |
0.0065 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 400 V | 400 V | M; IEC 60112 |
| 500 V | 500 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |
| Zone 3 | 240 - 270 °C | 464 - 518 °F | |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6
- SABIC PP 6711K Polypropylene Copolymer for Injection Molding
- Kleerdex Kydex® P90 Acrylic/PVC Extrusion Compound (discontinued **)
- DuPont Selar® RB 421 EVOH Barrier Resin (discontinued **)
- Garlock GYLON® 3545 Layered Microcellular PTFE Gasketing
- Sekisui PIOCELAN OP-30EU (Low VOC, Low odor) Moldable Polymer Foam
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- Dow Corning XIAMETER® PMCPPMX-200 2CS Silicone Fluid
- DuPont Teijin Films Melinex® FRPS Polyester Film, 142 Gauge
- Hippe PVC-U Polyvinyl Chloride
Copyright © lookpolymers.com All Rights Reserved