EPICHEM PA 66 Polyamide 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | EPICHEM srl |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM PA 66 Polyamide 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 8.0 % @Temperature 23.0 °C |
8.0 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 100 | 100 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ASTM D638, ISO R527 |
| Elongation at Break | 40 % | 40 % | ASTM D638, ISO R527 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.400 - 0.600 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.749 - 1.12 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 85.0 °C | 185 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 200 °C | 392 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 225 °C @Load 5.00 kg |
437 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 240 °C @Load 0.999 kg |
464 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.5 @Frequency 1000 Hz |
3.5 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 110 kV/mm | 2790 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Indium Corp. 42-SS Soldering Flux
- Karina E 851-48/1-F-ISM Black PVC Compound
- Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Dry)
- Saint-Gobain CHR® C Film Backing Silicone Adhesive Pressure Sensitive Tape
- Terio Corporation TZOH-60 Zirconium Hydroxide
- Elektro-Isola G-Etronax EP 22 Epoxy, Glass Fabric Reinforcement, Light Yellow, Tubes
- Ensinger Tecapeek® XP-113 Compression Molded PEEK Compound, 10% PTFE, 15% Graphite, and 3% Carbon Fiber
- Asahi Kasei Xyron® G702H Modified Polyphenylene Ether
- Akzo Nobel Expancel® 950 DU 120 Dry unexpanded microspheres
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 288°C Temper
Copyright © lookpolymers.com All Rights Reserved