- Lanxess Durethan® B 31 FCS 000000 Nylon 6, Film Grade
Lanxess Durethan® B 31 FCS 000000 Nylon 6, Film Grade
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® B 31 FCS 000000 Nylon 6, Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, non-reinforced, extrusion, low viscosity, slip agentInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 10 % | 10 % | ISO 62 |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 235 °C |
16 g/10 min @Load 4.76 lb, Temperature 455 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 50.0 MPa | 7250 psi | ISO 2039-1 |
| 140 MPa | 20300 psi | ISO 2039-1 | |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | cond.; ISO 527-1, -2; 50 mm/min |
| 75.0 MPa | 10900 psi | d.a.m.; ISO 527-1, -2; 50 mm/min | |
| Elongation at Break | 20 % | 20 % | d.a.m.; ISO 527-1, -2; 50 mm/min |
| >= 50 % | >= 50 % | cond.; ISO 527-1, -2; 50 mm/min | |
| Elongation at Yield | 4.0 % | 4.0 % | d.a.m.; ISO 527-1, -2; 50 mm/min |
| 25 % | 25 % | cond.; ISO 527-1, -2; 50 mm/min | |
| Tensile Modulus | 0.800 GPa | 116 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 2.80 GPa | 406 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 20.0 MPa @Strain 3.50 % |
2900 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 90.0 MPa @Strain 3.50 % |
13100 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 0.700 GPa | 102 ksi | cond., 2 mm/min; ISO 178-A |
| 2.60 GPa | 377 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A | |
| 7.50 kJ/m² @Temperature -30.0 °C |
3.57 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1A | |
| 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
d.a.m.; ISO 180-1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 180-1U | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
d.a.m.; ISO 180-1U | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
cond.; ISO 180-1U | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| Charpy Impact, Notched | <= 0.500 J/cm² @Temperature -30.0 °C |
<= 2.38 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA | |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1, -2 |
| Vicat Softening Point | 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | for test specimens; ISO 294 |
| Mold Temperature | 40.0 °C | 104 °F | for test specimens; ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6, ES, 14-030 |
Users viewing this material also viewed the following:
- Nye Lubricants 773A (NG) Synthetic Oil
- SABIC Innovative Plastics Lexan® HPX8REU PC Copolymer (Europe-Africa-Middle East)
- Kennametal Stellite Stoody® 5 Cobalt-Base Cast Alloy
- Glastic Laminates/Shapes 1580 Polyester Laminate
- SABIC Innovative Plastics LNP STAT-KON DE002ER PC
- Solvay Specialty Polymers Hyflon® PFA P220 Perfluoroalkoxy (PFA)
- Saint-Gobain CHR® SG15-05(R) High Performance Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Styron CALIBREâ„¢ 2061-15 Polycarbonate
- Dow Corning SYL-OFF® PMCP7923 Catalyst Emulsion
- BASF Ultramid® B3GM35 Q643 15/25% Glass/Mineral Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved