SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* WC006 is a compound based on PBT resin containing 30% Carbon Fiber. Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0023 cm/cm @Time 86400 sec |
0.0023 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 - 0.020 cm/cm @Time 86400 sec |
0.010 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
| 158 MPa | 22900 psi | ISO 527 | |
| Tensile Strength, Yield | 158 MPa | 22900 psi | ASTM D638 |
| 158 MPa | 22900 psi | ISO 527 | |
| Elongation at Break | 1.2 % | 1.2 % | ASTM D638 |
| 1.2 % | 1.2 % | ISO 527 | |
| Elongation at Yield | 1.2 % | 1.2 % | ASTM D638 |
| 1.2 % | 1.2 % | ISO 527 | |
| Tensile Modulus | 19.99 GPa | 2899 ksi | 50 mm/min; ASTM D638 |
| 20.66 GPa | 2996 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| 219 MPa | 31800 psi | ISO 178 | |
| Flexural Modulus | 15.16 GPa | 2199 ksi | ASTM D790 |
| 17.0 GPa | 2470 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.64 J/cm | 8.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.67 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 12.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.67 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 211 °C @Thickness 3.20 mm |
412 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- 3M Dyneon™ Fluorel™ FC-2180 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Lubrizol Advanced Materials PEARLBOND® 123 Linear Thermoplastic Polyurethane
- Techmer ES HiFill® PA11 GL8 HS UV
- Tipco Tipcolite® VASW 200 Phenolic Compound, Long Glass Fiber, in fluffy form, Medium -Soft Flow & Very High Strength
- A. Schulman POLYFORT™ FPP 3708U UV Stable Copolymer Polypropylene
- Covestro Makroblend® UT5205 PC/PBT Blend
- Aclo Accutech Polypropylene Homopolymer HP0336W20L Wollastonite Reinforced
- Plastcom SLOVALEN PQ 83 T 10 PP, 10% mineral filling
Copyright © lookpolymers.com All Rights Reserved