DuPont Performance Polymers Zytel® FG42L NC010 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® FG42L NC010 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | |
| Water Absorption | 8.5 % @Thickness 2.00 mm |
8.5 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Moisture Absorption | 2.60 % @Thickness 2.00 mm |
2.60 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Viscosity Test | 280 cm³/g | 280 cm³/g | DAM; ISO 307 1157 1628 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | DAM; ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | DAM; ISO 294-4 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50%RH; ISO 527-1/-2 |
| 83.0 MPa | 12000 psi | DAM; ISO 527-1/-2 | |
| Elongation at Break | 40 % | 40 % | DAM; Nominal; ISO 527-1/-2 |
| >= 50 % | >= 50 % | 50%RH; Nominal; ISO 527-1/-2 | |
| Elongation at Yield | 5.0 % | 5.0 % | DAM; ISO 527-1/-2 |
| 27 % | 27 % | 50%RH; ISO 527-1/-2 | |
| Tensile Modulus | 1.20 GPa | 174 ksi | 50%RH; ISO 527-1/-2 |
| 3.10 GPa | 450 ksi | DAM; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | 50%RH; ISO 179/1eU |
| NB | NB | DAM; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | DAM; ISO 179/1eA |
| 2.00 J/cm² | 9.52 ft-lb/in² | 50%RH; ISO 179/1eA | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |
| 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | DAM; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | DAM; ISO 11359-1/-2 |
| Specific Heat Capacity | 2.79 J/g-°C | 0.667 BTU/lb-°F | |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | of melt |
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | DAM; ISO 75-1/-2 |
| Vicat Softening Point | 244 °C | 471 °F | DAM; 50°C/h 50N; ISO 306 |
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | DAM; 10°C/min; ISO 11357-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 |
| V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
DAM; IEC 60695-11-10 | |
| Oxygen Index | 28 % | 28 % | DAM; ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | 50%RH; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DAM; IEC 60093 | |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
DAM; IEC 60250 |
| 4.2 @Frequency 1.00e+6 Hz |
4.2 @Frequency 1.00e+6 Hz |
50%RH; IEC 60250 | |
| 4.3 @Frequency 100 Hz |
4.3 @Frequency 100 Hz |
DAM; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
50%RH; IEC 60250 | |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | DAM; IEC 60243-1 |
| Dissipation Factor | 0.015 @Frequency 100 Hz |
0.015 @Frequency 100 Hz |
DAM; IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
DAM; IEC 60250 | |
| 0.075 @Frequency 1.00e+6 Hz |
0.075 @Frequency 1.00e+6 Hz |
50%RH; IEC 60250 | |
| 0.20 @Frequency 100 Hz |
0.20 @Frequency 100 Hz |
50%RH; IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Delivery Form | Pellets | |
| Processing | Casting | |
| Coatable | ||
| Film Extrusion | ||
| Injection Moulding | ||
| Other Extrusion | ||
| Profile Extrusion | ||
| Sheet Extrusion | ||
| Regional Availability | Asia Pacific | |
| Europe | ||
| Global | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C2800 PC+ABS
- PolyOne Geon™ 170 Series 4195 Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Global D-2024 Low Density Polyethylene, Film Extrusion Grade (discontinued **)
- Chevron Phillips Marlex® C514 HDPE Pipe and Corrugated Extrusion Resin (discontinued **)
- Star Plastics PCGF10 Molding Grade PC with 10% Glass
- Skamol Group SKAMOBAR 69 Low-Alumina Fireclay Brick
- DSM Arnite® TV6 220 PBT-GF10
- Carpenter Micro-Melt® 10 Hardened and Tempered Tool Steel (AISI A11)
- AIM 47 Fusible Bismuth Alloy
- A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved