DuPont Performance Polymers Zytel® E53 NC010 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® E53 NC010 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® E53 NC010 is a very high viscosity polyamide 66 resin for extrusion.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
| Water Absorption | 2.7 % @Temperature 23.0 °C |
2.7 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 8.5 % @Temperature 23.0 °C |
8.5 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to | |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 2.00 mm |
0.016 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C |
7980 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 84.0 MPa @Temperature 23.0 °C |
12200 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
50%RH; nominal; ISO 527 |
| >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 | |
| >= 100 % @Temperature 23.0 °C |
>= 100 % @Temperature 73.4 °F |
50%RH; nominal; ISO 527 | |
| Elongation at Yield | 4.4 % @Temperature 23.0 °C |
4.4 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 30 % @Temperature 23.0 °C |
30 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 1.20 GPa @Temperature 23.0 °C |
174 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
50%RH; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA | |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| Melting Point | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | DAM; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm @Temperature 23.0 °C |
1.00e+13 ohm-cm @Temperature 73.4 °F |
DAM; IEC 60093 |
| Dielectric Constant | 3.9 @Frequency 100 Hz, Temperature 23.0 °C |
3.9 @Frequency 100 Hz, Temperature 73.4 °F |
DAM; IEC 60250 |
| Dissipation Factor | 0.010 @Frequency 100 Hz, Temperature 23.0 °C |
0.010 @Frequency 100 Hz, Temperature 73.4 °F |
DAM; IEC 60250 |
| Comparative Tracking Index | 600 V @Temperature 23.0 °C |
600 V @Temperature 73.4 °F |
50%RH; IEC 60112 |
| 600 V @Temperature 23.0 °C |
600 V @Temperature 73.4 °F |
DAM; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum |
| 280 - 300 °C | 536 - 572 °F | DAM | |
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA66< | ISO 11469; DAM |
| Processing Method | Extrusion | DAM |
| Product Category | Extrusion Resins | DAM |
| Unreinforced Resins | DAM | |
| Resin Identification | PA66 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
Users viewing this material also viewed the following:
- MV Labs SR1000 SrSO4 Strontium sulfate
- PolyOne Maxxam™ PPR-30G Black Polypropylene Homopolymer (PP Homopolymer)
- Fiberfil® J-60/30/F Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled
- Lubriplate Vacuum Pump Oil Light Specialty Oil and Fluid
- Solvay Specialty Polymers Lavanta® 5115 WH 011 Polyester, High Performance (HPP), 15% Glass Fiber
- Daikin DAI-EL G-555 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 69% Fluorine Content
- DuPont Performance Polymers Rynite® 540SUV BK544 Polyethylene Terephthalate (PET) (Unverified Data**)
- Barlog Plastics KEBAFORM C 274 VT POM Copolymer unreinforced, antistatic
- DuPont Performance Polymers Zytel® FE5382 BK276 Nylon 612 (Unverified Data**)