LyondellBasell Higlass SB224-3 Polypropylene Copolymer, 30% Glass Fiber

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer LyondellBasell
Trade Name Higlass
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Higlass SB224-3 Polypropylene Copolymer, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key Features: conventional melt flow, medium high modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high impact strength, high stiffness, good processabilityApplications: wheel well housings, garden equipment housings, recreational vehicle componentsDescription: Higlass SB224-3 conventional melt flow, chemically coupled, 30% glass fiber-reinforced polypropylene copolymer has an excellent balance of strength, stiffness and impact resistance.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
Tool, Montell
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 66.0 MPa
9570 psi
ASTM D638
Elongation at Break 8.0 %
8.0 %
ASTM D638
Flexural Modulus 3.90 GPa
566 ksi
Tangent at 0.05 in/min; ASTM D790A
Izod Impact, Notched 2.40 J/cm
4.50 ft-lb/in
ASTM D256A
Izod Impact, Unnotched 8.00 J/cm
15.0 ft-lb/in
ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 155 °C
311 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
ASTM D648
UL RTI, Mechanical with Impact 110 °C

@Thickness 1.60 mm
230 °F

@Thickness 0.0630 in
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in