PolyOne Geon™ Vinyl Rigid Molding M4885 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Molding M4885 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 88.9 cm | 35.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | ASTM D2240 |
| Tensile Strength, Yield | 43.4 MPa | 6290 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 68.9 MPa | 9990 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 5.90 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
11.1 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Injection Molded; ASTM D256A |
| 8.50 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
15.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C @Thickness 6.35 mm |
160 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 72.8 °C @Thickness 6.35 mm |
163 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 6.35 mm |
153 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 72.2 °C @Thickness 6.35 mm |
162 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746 |
| Flammability, UL94 | V-0 @Thickness 1.80 mm |
V-0 @Thickness 0.0709 in |
ALL; UL 94 |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
ALL; UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % @Thickness 3.81 mm |
8.0 % @Thickness 0.150 in |
ASTM D1003 |
| Transmission, Visible | 79 % @Thickness 3.81 mm |
79 % @Thickness 0.150 in |
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 199 - 204 °C | 390 - 399 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Features | High Flow | |
| Low Temperature Impact Resistance | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Electrical/Electronic Applications | |
| Telecommunications |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB MS-500 Solid Complex Stabilizer
- Teknor Apex APEX® 90-A472R-65-NT Polyvinyl Chloride, Flexible
- Styron CALIBREâ„¢ 7101 8 Polycarbonate, 10% Glass Reinforced
- Samyang Trirex® DMH3000S Polycarbonate, High Flow Flame Retardancy
- Valley Adhesives EM-240 Low Temperature Application Glue Stick
- Dow Corning LSPRD13 SILICONE MASTERBATCH RED
- Fainplast Compounds CL 006 Flexible PVC, Sheathing
- Adell AS-10 Nylon 66, General Purpose
- ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, Annealed at 982°C (1800°F), UNS N06601
Copyright © lookpolymers.com All Rights Reserved