Kolon KOCETAL® GF105 G/F Reinforced Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Kolon |
| Trade Name | Kocetal® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOCETAL® GF105 G/F Reinforced Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforced, improved stiffness. Applications: Products for high stiffness, improved fatigue properties. Information provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Melt Flow | 2.6 g/10 min | 2.6 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength | 120 MPa | 17400 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 175 MPa | 25400 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C | 13.9 µin/in-°F | ASTM D696 |
| Melting Point | 166 °C | 331 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1855 TPE, PP Overmold or Standalone use
- Pau Tai Unistab ECZ-81 Calcium-Zinc/Barium-Zinc
- Global EPP PA 6C HS BLUE Cast Polyamide 6 + UV and Heat Stabilizers
- Momentive Performance Materials Addisilâ„¢ 442 E Healthcare Extrusion Grade Heat Cured Rubber
- Solvay Specialty Polymers Veradel® 3500 Polyethersulfone (PESU)
- Teknor Apex Monprene® MP-2287N Thermoplastic Elastomer
- ATI Allegheny Ludlum S7 Tool Steel, UNS T41907
- Barlog Plastics KEBAFLEX SG 60 A.01 TPE-S, Shore A60, natural
- ExxonMobil 625 Mobil SHC 600 Series
- Eastman D4041-P Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved