DuPont Performance Polymers Delrin® FG400MTD BLA079 Acetal (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® FG400MTD BLA079 Acetal (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Delrin® FG400MTD BLA079 is a metal filled, medium viscosity acetal copolymer for injection molding. It is detected in metal detectors. It has been developed for consideration into applications such as parts for the food industry.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.53 g/cc	0.0553 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.017 cm/cm @Thickness 2.00 mm	0.017 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.016 cm/cm @Thickness 2.00 mm	0.016 in/in @Thickness 0.0787 in	ISO 294-4
Melt Flow	17 g/10 min @Load 2.16 kg, Temperature 190 °C	17 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	61.0 MPa @Temperature 23.0 °C	8850 psi @Temperature 73.4 °F	ISO 527
Elongation at Yield	8.0 % @Temperature 23.0 °C	8.0 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	2.80 GPa @Temperature 23.0 °C	406 ksi @Temperature 73.4 °F	ISO 527
Flexural Modulus	2.70 GPa @Temperature 23.0 °C	392 ksi @Temperature 73.4 °F	ISO 178
Charpy Impact Unnotched	7.00 J/cm² @Temperature 23.0 °C	33.3 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.300 J/cm² @Temperature 23.0 °C	1.43 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	500 µm/m-°C @Temperature -40.0 - 23.0 °C	278 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 23.0 - 55.0 °C	278 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	500 µm/m-°C @Temperature 55.0 - 100 °C	278 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C @Temperature -40.0 - 23.0 °C	55.6 µin/in-°F @Temperature -40.0 - 73.4 °F	ISO 11359-1/-2
	120 µm/m-°C @Temperature 23.0 - 55.0 °C	66.7 µin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
	150 µm/m-°C @Temperature 55.0 - 100 °C	83.3 µin/in-°F @Temperature 131 - 212 °F	ISO 11359-1/-2
Melting Point	168 °C	334 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	100 °C	212 °F	ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	205 °C	401 °F	Optimum; Injection Molding
	200 - 210 °C	392 - 410 °F	Injection Molding
Mold Temperature	90.0 °C	194 °F	optimum; Injection Molding
	80.0 - 100 °C	176 - 212 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.20 %	<= 0.20 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Natural Color
Forms	Pellets
Generic	Acetal (POM) Copolymer
Material Status	Preliminary Data
Processing Method	Injection Molding
Product Category	Food Contact Resins
	Metal Filled Resins
Region Available - Global	Yes
RoHS Compliance	Contact Manufacturer
Uses	Food Applications, Non-specific