SABIC Innovative Plastics LNP Thermocomp PFB42ES PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp PFB42ES PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PFB42ES is a compound based on PA6 resin containing Glass Fiber, Glass Bead. Added features include: Easy Molding, Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 1.9 % @Temperature 23.0 °C, Time 86400 sec |
1.9 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0044 cm/cm | 0.0044 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 93.0 MPa | 13500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 4.4 % | 4.4 % | Flexural Strain, 2 mm/min; ISO 178 | |
| Tensile Modulus | 5.70 GPa | 827 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 49.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
27.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 93.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
51.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Materion Beryllium Copper Alloy 25 Rod and Bar; H (TD04) Temper; up to 9.5 mm (UNS C17200)
- LyondellBasell Pro-faxâ„¢ PH350 Polypropylene Homopolymer
- SABIC Innovative Plastics LNP THERMOCOMP EX93452 PEI (Asia Pacific)
- Samsung Cheil Industries Infino® NH-1023P PC, Unreinforced FR
- Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry)
- ExxonMobil Enable™ 23-05HH Metallocene Polyethylene Resin
- Crucible Steel 174 SXR Precipitation Hardening Stainless Steel
- BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved