SABIC Innovative Plastics LNP THERMOCOMP MX95318 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MX95318 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MX95318 is a compound based on Polypropylene containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 5.00 MPa | 725 psi | 5 mm/min; ISO 527 |
| 20.0 MPa | 2900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 5 mm/min; ISO 527 |
| 30.0 MPa | 4350 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 29 % | 29 % | Type I, 5 mm/min; ASTM D638 |
| 40 % | 40 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 7.0 % | 7.0 % | 5 mm/min; ISO 527 |
| 7.5 % | 7.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.75 GPa | 254 ksi | 1 mm/min; ISO 527 |
| 2.08 GPa | 302 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 37.0 MPa | 5370 psi | ISO 178 |
| Flexural Modulus | 1.65 GPa | 239 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.69 GPa | 245 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.220 J/cm | 0.412 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.25 J/cm | 7.96 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 78.0 °C @Thickness 3.20 mm |
172 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Fujipoly Industries Sarcon® 30GTR Thin-Film GTR
- Lushan WR-2 Wood Plastic Composites Compatibilizer
- Karina 600D48/1-C-IS Black PVC Compound
- Teknor Apex APEX® 80-C131E-NT Polyvinyl Chloride, Flexible
- Dow AMPLIFY™ EA 100 Ethylene-ethyl Acrylate (EEA)
- Clariant Renol PA113C Nylon 66, Molybdenum Disulfide Lubricated
- Colorite Polymers 7077 Non-Phthalate 77 Series Vinyl Compound
- AK Steel TRAN-COR® H-1 CARLITE® Grain Oriented Electrical Steel
- 3M 467MPF High Performance Adhesive Transfer Tapes with Adhesive 200MP
- Lubrizol Advanced Materials Pearlstick® D40-70/03 Linear Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved