Material Notes:

Delrin® 100T BK602 is a toughened, high viscosity acetal homopolymer grade with superior impact resistance. It is designed for highly stressed parts where outstanding toughness is required.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ISO 1183
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	54.0 MPa @Temperature 23.0 °C	7830 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	>= 50 % @Temperature 23.0 °C	>= 50 % @Temperature 73.4 °F	nominal; ISO 527
	>= 50 % @Temperature 23.0 °C	>= 50 % @Temperature 73.4 °F	50mm/min; ISO 527
Elongation at Yield	27 % @Temperature 23.0 °C	27 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	1.90 GPa @Temperature 23.0 °C	276 ksi @Temperature 73.4 °F	ISO 527
Charpy Impact, Notched	1.10 J/cm² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	2.30 J/cm² @Temperature 23.0 °C	10.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	71.0 °C	160 °F	ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	205 °C	401 °F	Optimum; Injection Molding
	200 - 210 °C	392 - 410 °F	Injection Molding
Mold Temperature	50.0 °C	122 °F	optimum; Injection Molding
	40.0 - 60.0 °C	104 - 140 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F	Injection Molding
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
Moisture Content	<= 0.050 %	<= 0.050 %	Injection Molding

Descriptive Properties	Value	Comments
Appearance	Black Color
Extrudable - Coating	Yes
Extrudable - Tubing	Yes
Extrudable - Wire and Cable	Yes
Extrusion Blow Moldable	Yes
Features	Homopolymer
	Impact Modified
	Impact Resistance, High
	Molecular Wt., High
	Toughness, Ultra High
	Viscosity, High
Forms	Pellets
Generic	Acetal (POM) Homopolymer
Material Status	Current
Part Marking Code	>POM-I<	ISO 11469
Polymer Family	POM
Polymer Type	POM Homopolymer
Processing Method	Extrusion
	Injection Molding
Product Category	Extrusion Resins
	Toughened Resins
	Unreinforced Resins
Region Available - Global	Yes
Resin Identification	POM-I	ISO 1043
RoHS Compliance	Contact Manufacturer
Ultrasonic Weldable	Yes
Uses	Fasteners
	Fasteners
	Gears
	Parts, Engineering
	Tubing