SABIC Innovative Plastics LNP LUBRICOMP DL003 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DL003 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DL003 is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ASTM D792
1.28 g/cc
0.0462 lb/in³
ISO 1183
Moisture Absorption 0.120 %
0.120 %
50% RH, 24 hrs; ASTM D570
0.150 %
0.150 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0083 cm/cm

@Time 86400 sec
0.0083 in/in

@Time 24.0 hour
ISO 294
0.0080 - 0.0090 cm/cm

@Time 86400 sec
0.0080 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0088 cm/cm

@Time 86400 sec
0.0088 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
ASTM D638
50.0 MPa
7250 psi
ISO 527
Tensile Strength, Yield 51.0 MPa
7400 psi
ASTM D638
53.0 MPa
7690 psi
ISO 527
Elongation at Break 37.6 %
37.6 %
ASTM D638
Elongation at Yield 5.5 %
5.5 %
ISO 527
6.1 %
6.1 %
ASTM D638
Tensile Modulus 2.06 GPa
299 ksi
50 mm/min; ASTM D638
2.20 GPa
319 ksi
1 mm/min; ISO 527
Flexural Strength 80.0 MPa
11600 psi
ASTM D790
84.0 MPa
12200 psi
ISO 178
Flexural Modulus 2.18 GPa
316 ksi
ASTM D790
2.40 GPa
348 ksi
ISO 178
Izod Impact, Notched 2.77 J/cm
5.19 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 28.0 kJ/m²
13.3 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 137 kJ/m²
65.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 30.0 J
22.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 34.0 J
25.1 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.18
0.18
ASTM D3702 Modified
Coefficient of Friction, Static 0.070
0.070
ASTM D3702 Modified
K (wear) Factor 121 x 10-8 mm³/N-M
60.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
127 °C

@Thickness 3.20 mm
261 °F

@Thickness 0.126 in
unannealed; ASTM D648