DuPont Performance Polymers Delrin® 100AL NC010 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 100AL NC010 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® 100AL NC010 an unreinforced, high viscosity, lubricated acetal homopolymer resin, containing an advanced system of lubrication for low wear and friction against metals and plastics.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.020 cm/cm

@Thickness 2.00 mm
0.020 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.018 cm/cm

@Thickness 2.00 mm
0.018 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Melt Index of Compound 1.7 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.7 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 70.0 MPa

@Temperature 23.0 °C
10200 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 45 %

@Temperature 23.0 °C
45 %

@Temperature 73.4 °F
nominal; ISO 527
65 %

@Temperature 23.0 °C
65 %

@Temperature 73.4 °F
50mm/min; ISO 527
Elongation at Yield 18 %

@Temperature 23.0 °C
18 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 3.00 GPa

@Temperature 23.0 °C
435 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 2.80 GPa

@Temperature 23.0 °C
406 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 17.0 J/cm²

@Temperature -30.0 °C
80.9 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
25.0 J/cm²

@Temperature 23.0 °C
119 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
278 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
278 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 100 °C
278 µin/in-°F

@Temperature 131 - 212 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature -40.0 - 23.0 °C
55.6 µin/in-°F

@Temperature -40.0 - 73.4 °F
ISO 11359-1/-2
110 µm/m-°C

@Temperature 23.0 - 55.0 °C
61.1 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1/-2
150 µm/m-°C

@Temperature 55.0 - 100 °C
83.3 µin/in-°F

@Temperature 131 - 212 °F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
ISO 75-1/-2
UL RTI, Electrical 50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
UL 746B
50.0 °C

@Thickness 0.750 mm
122 °F

@Thickness 0.0295 in
UL 746B
UL RTI, Mechanical with Impact 50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
UL 746B
50.0 °C

@Thickness 0.750 mm
122 °F

@Thickness 0.0295 in
UL 746B
UL RTI, Mechanical without Impact 50.0 °C

@Thickness 0.750 mm
122 °F

@Thickness 0.0295 in
UL 746B
50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
UL 746B
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL94
Processing Properties Metric English Comments
Melt Temperature 215 °C
419 °F
Optimum; Injection Molding
210 - 220 °C
410 - 428 °F
Injection Molding
Mold Temperature 90.0 °C
194 °F
optimum; Injection Molding
80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Moisture Content <= 0.20 %
<= 0.20 %
Injection Molding
Descriptive Properties Value Comments
Additive Lubricant
Appearance Natural Color
Drying Recommended Not normally required unless moisture content of resin exceeds recommended level
Features Creep Resistance, Good
Friction, Low
Homopolymer
Impact Resistance, High
Lubricated
Viscosity, High
Wear Resistance, Good
Forms Pellets
Generic Acetal (POM) Homopolymer
Material Status Current
Part Marking Code >POM-S<
ISO 11469
Polymer Family POM
Polymer Type POM Homopolymer
Processing Method Extrusion
Injection Molding
Product Category Extrusion Resins
Low Wear and Friction Resins
Unreinforced Resins
Region Available - Global Yes
Resin Identification POM-S
ISO 1043
RoHS Compliance Contact Manufacturer
Ultrasonic Weldable Yes
Uses Conveyors
Gears
Parts, Engineering