- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Diamond Polymers ABS TM 25
Diamond Polymers ABS TM 25
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS TM 25.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Heat Resistant Grade, Very High HeatInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 0.50 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.50 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 1.9 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.9 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.34 GPa | 340 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
2.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 112 °C | 234 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 117 °C | 242 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- Kotec Carbotex K-20UV30 Polycarbonate, General Purpose, UV Stability Grade
- Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure
- Styron DL 395PA Modified SB
- Borealis FT5231 Low Density Polyethylene
- Polyram RamTough RZ321G2 Polycarbonate, 10% Glass Fiber, Flame Retardant
- Eastman Tenite Butyrate 264A3720013 Clear, Trsp Cellulose Acetate Butyrate
- Ensinger TECATRON™ PVX Polyphenylene sulfide (PPS), Bearing Grade
- Colorite Polymers 8011 Clear Extrusion Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved