Hexcel® HexPly® EF02 Epoxy Curing System after THR 120 EF01 S50 37% Curing Cycle
| Category | Polymer , Thermoset , Epoxy , Epoxy Cure Resin |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® EF02 Epoxy Curing System after THR 120 EF01 S50 37% Curing Cycle.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 1280.9 MPa @Temperature 50.0 °C |
185780 psi @Temperature 122 °F |
Flexure Long; 30 min @ 250°F; prEN 2563 |
| 1381.0 MPa @Temperature 50.0 °C |
200290 psi @Temperature 122 °F |
Flexure Long; 15 min @ 250°F; prEN 2563 | |
| 1531.0 MPa @Temperature 22.8 °C |
222060 psi @Temperature 73.0 °F |
Flexure Long; 15 min @ 250°F; prEN 2563 | |
| 1611.1 MPa @Temperature 22.8 °C |
233670 psi @Temperature 73.0 °F |
Flexure Long; 30 min @ 250°F; prEN 2563 | |
| Flexural Modulus | 91.08 GPa @Temperature 50.0 °C |
13210 ksi @Temperature 122 °F |
Flexure Long; 30 min @ 250°F; prEN 2563 |
| 93.1 GPa @Temperature 22.8 °C |
13500 ksi @Temperature 73.0 °F |
Flexure Long; 15 min @ 250°F; prEN 2563 | |
| 93.1 GPa @Temperature 22.8 °C |
13500 ksi @Temperature 73.0 °F |
Flexure Long; 30 min @ 250°F; prEN 2563 | |
| 93.1 GPa @Temperature 50.0 °C |
13500 ksi @Temperature 122 °F |
Flexure Long; 15 min @ 250°F; prEN 2563 | |
| Shear Strength | 57.0 MPa @Temperature 50.0 °C |
8270 psi @Temperature 122 °F |
ILSS Weft; 30 min @ 250°F |
| 60.1 MPa @Temperature 50.0 °C |
8710 psi @Temperature 122 °F |
ILSS Weft; 15 min @ 250°F | |
| 78.05 MPa @Temperature 22.8 °C |
11320 psi @Temperature 73.0 °F |
ILSS Long; 30 min @ 250°F | |
| 80.05 MPa @Temperature 22.8 °C |
11610 psi @Temperature 73.0 °F |
ILSS Long; 15 min @ 250°F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 18.0 Month @Temperature -17.7 °C |
18.0 Month @Temperature 0.140 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® NX07353 PC+ABS (Asia Pacific)
- Lubriplate FMO 150 AW USP Mineral Oil-Based Food Machinery Grade Oil
- Karina 850-10/179-Y-ERYM-PO White PVC Compound
- SABIC Innovative Plastics Valox® 553 PBT (Europe-Africa-Middle East)
- SABIC Innovative Plastics Xenoy® 6620U PBT+PC
- Struktol STRUKSILON 8101 Silicone Stabilizer for PU-Rigid Foam
- Zeon Chemicals Nipol® 40-5 Nitrile Elastomer
- Dow Corning SILASTIC® 7-4860 BIOMEDICAL GRADE LSR, KIT
- ExxonMobil 632 Mobilgear 600 Series
- Americas Styrenics STYRON® 665 High Heat Crystal Polystyrene
Copyright © lookpolymers.com All Rights Reserved