DSM Stanyl® 46SF5030 PA46-GF30 FR(17)
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Flame Retarded + Glass Fiber Reinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Stanyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Stanyl® 46SF5030 PA46-GF30 FR(17).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.60 % | 1.60 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
| 170 MPa | 24700 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 1.9 % | 1.9 % | dry; ISO 527-1/-2 |
| 2.8 % | 2.8 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 7.50 GPa | 1090 ksi | cond; ISO 527-1/-2 |
| 12.0 GPa | 1740 ksi | dry; ISO 527-1/-2 | |
| Flexural Modulus | 6.80 GPa | 986 ksi | cond; ISO 178 |
| 11.0 GPa | 1600 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| V-0 @Thickness 0.350 mm |
V-0 @Thickness 0.0138 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | cond; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 225 V | 225 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- NYCOA ASN 27 300 KNF 30% Glass Fiber Reinforced, Heat Stabilized Nylon 6 Resin
- PolyOne Bergamid™ A70 GK30 black 13539126 Polyamide 66 (Nylon 66)
- Reltek BONDiT™ C-52 Bonding Agent, Adhesive and Primer
- MarkeTech Silicon Single Crystal Semiconductor Wafer, p-type, Dopant: NDT, Float Zone Grown
- Teknor Apex APEX® 3211-70 Polyvinyl Chloride, Flexible
- SPHERE ONE EXTENDOSPHERESâ„¢ PM 6550 Hollow Plastic Spheres
- A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin
- Arlon 0.029" (0.7366 mm) Flexible Heater Silicone with Fiberglass Substrate (55589R028)
- DuPont Performance Polymers Neoprene 750 Polychloroprene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved