Beijing Chemical Industry KAIFA® 302-G0 PBT Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® 302-G0 PBT Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 0.280 J/cm @Thickness 3.20 mm |
0.525 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Dielectric Polymers NT-140A89 General Purpose Laminating Adhesive (discontinued **)
- Huntsman AVALON® 95 AE Thermoplastic Polyurethane
- Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched
- SABIC Innovative Plastics Ultem HU1000E PEI (Europe-Africa-Middle East)
- Styron CALIBREâ„¢ 200-14 Polycarbonate Resin
- ExxonMobil LLDPE LL 1002.09 Linear Low Density Polyethylene Resin
- Dow AFFINITY™ SE 1400 Polyolefin Plastomer
- Saint-Gobain Meldin® 1277 Thermoplastic Bearing Material
Copyright © lookpolymers.com All Rights Reserved