SABIC Innovative Plastics Ultem MD131A PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem MD131A PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, enhanced flow Polyetherimide (Tg 217C). US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 6.60 kg, Temperature 337 °C |
16 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 70 % | 70 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 3.72 GPa | 540 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 165 MPa | 23900 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 3.72 GPa | 540 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 19.22 J/cm @Thickness 3.20 mm |
36.01 ft-lb/in @Thickness 0.126 in |
reverse notched; ASTM D 256 |
| Gardner Impact | 23.0 J @Temperature 23.0 °C |
17.0 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten, PLC code 5; ASTM D 495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | PLC code 4; UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | PLC code 1; UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | surface, PLC code 3; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | PLC code 2; UL 746A |
Users viewing this material also viewed the following:
- Polimeros Mexicanos Rotolene® 93050 Medium Density Polyethylene
- Gouda Vuurvast ADHESIET 180 PCr Dry Air-Setting Refractory Mortar
- Momentive Performance Materials RTV5249 Gray Adhesive Sealant, Fast Cure Paste
- Techmer ES HiFill® POM 0223 B Acetal
- Saint-Gobain Chemfab® 6 Premium PTFE-Coated Glass
- Zhejiang Juner PA-A7-1 Flame-Retardant & Glass Reinforced, Environmental PA66
- Trelleborg AEM Eccospheres® IGD-101 Sodium Borosilicate Glass Microspheres
- EMS-Grivory Grivory® EBV-2H PA6-GF20
- ChevronTexaco Texcool® P-155
- ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 50% Cold Work
Copyright © lookpolymers.com All Rights Reserved