Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

DSM Stanyl® 46HF4550 PA46-GF50

Category Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced
Manufacturer DSM Engineering Plastics
Trade Name Stanyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Stanyl® 46HF4550 PA46-GF50.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
dry; ISO 1183
Moisture Absorption 1.85 %
1.85 %
Sim. To ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
Sim. To ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 170 MPa
24700 psi
cond; ISO 527-1/-2
250 MPa
36300 psi
dry; ISO 527-1/-2
135 MPa

@Temperature 160 °C
19600 psi

@Temperature 320 °F
ISO 527-1/-2
150 MPa

@Temperature 120 °C
21800 psi

@Temperature 248 °F
ISO 527-1/-2
Elongation at Break 2.2 %
2.2 %
dry; ISO 527-1/-2
3.5 %
3.5 %
cond; ISO 527-1/-2
3.5 %

@Temperature 120 °C
3.5 %

@Temperature 248 °F
ISO 527-1/-2
3.5 %

@Temperature 160 °C
3.5 %

@Temperature 320 °F
ISO 527-1/-2
Tensile Modulus 11.0 GPa
1600 ksi
cond; ISO 527-1/-2
16.0 GPa
2320 ksi
dry; ISO 527-1/-2
10.0 GPa

@Temperature 160 °C
1450 ksi

@Temperature 320 °F
ISO 527-1/-2
11.0 GPa

@Temperature 120 °C
1600 ksi

@Temperature 248 °F
ISO 527-1/-2
Flexural Modulus 11.0 GPa
1600 ksi
cond; ISO 178
15.0 GPa
2180 ksi
dry; ISO 178
Charpy Impact Unnotched 7.00 J/cm²

@Temperature -30.0 °C
33.3 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eU
7.00 J/cm²

@Temperature -30.0 °C
33.3 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eU
10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eA
1.80 J/cm²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 295 °C
563 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
dry; ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
dry; IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
dry; IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
cond; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
dry; IEC 60093
Dielectric Strength 25.0 kV/mm
635 kV/in
cond; IEC 60243-1
30.0 kV/mm
762 kV/in
dry; IEC 60243-1
Comparative Tracking Index 450 V
450 V
dry; IEC 60112