SCG Chemicals EL-Proâ„¢ P440J Polypropylene Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Pro™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Proâ„¢ P440J Polypropylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:Excellent impact strengthSuitable for small to medium partsRecommended Applications:High impact and durable automotive, motorcycle and electrical appliance parts such as fan stand, motor back coverIndustrial containers such as paint pailsInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Linear Mold Shrinkage, Flow | 0.0119 cm/cm @Thickness 2.00 mm |
0.0119 in/in @Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.0105 cm/cm @Thickness 2.00 mm |
0.0105 in/in @Thickness 0.0787 in |
TPE Method |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 26.5 MPa | 3840 psi | ASTM D638 |
| Elongation at Break | 520 % | 520 % | ASTM D638 |
| Flexural Modulus | 1.13 GPa | 164 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Temperature -20.0 °C |
0.918 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| 0.588 J/cm @Temperature 0.000 °C |
1.10 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 1.18 J/cm @Temperature 23.0 °C |
2.20 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | ASTM D746 |
| Flammability, UL94 | HB | HB |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 80 % @Thickness 1.00 mm |
80 % @Thickness 0.0394 in |
ASTM D1003 |
| Gloss | 30 % @Thickness 1.00 mm |
30 % @Thickness 0.0394 in |
ASTM D2457 |
Users viewing this material also viewed the following:
- Polikim ULPOLEN® 300 UHMWPE Standard
- Saint-Gobain Chemfab® 13 Premium PTFE-Coated Glass
- A. Schulman POLYBATCH™ Woodland Green 30233U/4 Concentrate Based In LLDPE
- EMS-Grivory Grivory® BG-40 S PA6-GF40
- 3M 3381 General Purpose Aluminum Foil Tape
- Adamas Adalon® 902 PTFE, 1% Conductive filler
- Ashley Polymers Ashlene® 935 Nylon 11
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber
- 3M Scotch-Weld™ DP405 Black Epoxy Adhesive
- LyondellBasell Astryn 65F5-4 Polypropylene Homopolymer, 40% Calcium Carbonate
Copyright © lookpolymers.com All Rights Reserved