DSM Novamid® 1010GN2-20 NAT/BK37 PA6-GF20 FR(17)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1010GN2-20 NAT/BK37 PA6-GF20 FR(17).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass Reinforced, Flame Retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.90 % | 1.90 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | dry; ISO 527-1/-2 |
| Elongation at Break | 2.1 % | 2.1 % | dry; ISO 527-1/-2 |
| Tensile Modulus | 9.20 GPa | 1330 ksi | dry; ISO 527-1/-2 |
| Flexural Strength | 155 MPa | 22500 psi | cond; ISO 178 |
| 205 MPa | 29700 psi | dry; ISO 178 | |
| Flexural Modulus | 5.50 GPa | 798 ksi | cond; ISO 178 |
| 7.70 GPa | 1120 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 3.80 J/cm² @Temperature 23.0 °C |
18.1 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.00e+14 ohm-cm | 8.00e+14 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 8.00e+12 ohm | 8.00e+12 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| Comparative Tracking Index | 225 V | 225 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM 525 General Purpose Polystyrene
- SABIC Innovative Plastics Lexan® ML7647 PC (Europe-Africa-Middle East)
- Gichem GILAC C120/T Acrylonitrile Butadiene Styrene (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP RF004XXD PA 66
- Tipco Tipcolite® TPF 1211 - Unreinforced Phenolic Resin having 53 mm Norton Flow with 12% Hexamine
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix
- Clariant Renol R60G33HSL Nylon 6, 33% Glass Fiber, Heat Stabilized, Lubricated, Economy
- Asahi Kasei Tenac®-C GN455 Copolymer Acetal Resin
- Ashley Polymers Ashlene® 830L-13G Nylon 6, 13% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved