DuPont Performance Polymers Zytel® 70G35HSLX BK357 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G35HSLX BK357 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G35HSLX BK357 is a 35% glass fiber reinforced heat stabilized black polyamide 66 for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
1.41 g/cc
0.0509 lb/in³
DAM; ISO 1183
Water Absorption 5.5 %

@Thickness 2.00 mm
 5.5 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.70 %

@Thickness 2.00 mm
 1.70 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 58900 cP

@Shear Rate 5000 1/s,
Temperature 305 °C
 58900 cP

@Shear Rate 5000 1/s,
Temperature 581 °F
 ISO 11403-1 -2
70480 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
 70480 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
 ISO 11403-1 -2
85520 cP

@Shear Rate 5000 1/s,
Temperature 285 °C
 85520 cP

@Shear Rate 5000 1/s,
Temperature 545 °F
 ISO 11403-1 -2
179600 cP

@Shear Rate 500 1/s,
Temperature 305 °C
 179600 cP

@Shear Rate 500 1/s,
Temperature 581 °F
 ISO 11403-1 -2
226700 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 226700 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
287300 cP

@Shear Rate 500 1/s,
Temperature 285 °C
 287300 cP

@Shear Rate 500 1/s,
Temperature 545 °F
 ISO 11403-1 -2
Viscosity Test 145 cm³/g
145 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
50%RH; ISO 527-1/-2
210 MPa
30500 psi
DAM; ISO 527-1/-2
Tensile Stress 16.01 MPa

@Strain 0.320 %,
Temperature 150 °C
 2322 psi

@Strain 0.320 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
18.0 MPa

@Strain 0.440 %,
Temperature 150 °C
 2610 psi

@Strain 0.440 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
26.14 MPa

@Strain 0.500 %,
Temperature 90.0 °C
 3791 psi

@Strain 0.500 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
27.47 MPa

@Strain 0.430 %,
Temperature 40.0 °C
 3984 psi

@Strain 0.430 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
30.18 MPa

@Strain 0.440 %,
Temperature 23.0 °C
 4377 psi

@Strain 0.440 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
33.18 MPa

@Strain 0.780 %,
Temperature 160 °C
 4812 psi

@Strain 0.780 %,
Temperature 320 °F
 DAM; ISO 11403-1 -2
35.5 MPa

@Strain 0.970 %,
Temperature 180 °C
 5150 psi

@Strain 0.970 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
37.48 MPa

@Strain 0.640 %,
Temperature 90.0 °C
 5436 psi

@Strain 0.640 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
40.44 MPa

@Strain 1.33 %,
Temperature 150 °C
 5865 psi

@Strain 1.33 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
50.14 MPa

@Strain 1.34 %,
Temperature 150 °C
 7272 psi

@Strain 1.34 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
50.17 MPa

@Strain 1.12 %,
Temperature 90.0 °C
 7277 psi

@Strain 1.12 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
54.49 MPa

@Strain 2.25 %,
Temperature 150 °C
 7903 psi

@Strain 2.25 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
55.94 MPa

@Strain 0.970 %,
Temperature 40.0 °C
 8113 psi

@Strain 0.970 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
57.46 MPa

@Strain 2.28 %,
Temperature 180 °C
 8334 psi

@Strain 2.28 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
58.23 MPa

@Strain 1.85 %,
Temperature 160 °C
 8446 psi

@Strain 1.85 %,
Temperature 320 °F
 DAM; ISO 11403-1 -2
61.0 MPa

@Strain 0.960 %,
Temperature 23.0 °C
 8850 psi

@Strain 0.960 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
65.05 MPa

@Strain 3.41 %,
Temperature 150 °C
 9435 psi

@Strain 3.41 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
66.63 MPa

@Strain 1.33 %,
Temperature 90.0 °C
 9664 psi

@Strain 1.33 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
67.97 MPa

@Strain 1.81 %,
Temperature 90.0 °C
 9858 psi

@Strain 1.81 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
70.03 MPa

@Strain 3.67 %,
Temperature 180 °C
 10160 psi

@Strain 3.67 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
70.06 MPa

@Strain 2.40 %,
Temperature 150 °C
 10160 psi

@Strain 2.40 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
73.95 MPa

@Strain 3.04 %,
Temperature 160 °C
 10730 psi

@Strain 3.04 %,
Temperature 320 °F
 DAM; ISO 11403-1 -2
76.99 MPa

@Strain 1.49 %,
Temperature 40.0 °C
 11170 psi

@Strain 1.49 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
77.13 MPa

@Strain 0.840 %,
Temperature 0.000 °C
 11190 psi

@Strain 0.840 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
78.05 MPa

@Strain 5.21 %,
Temperature 180 °C
 11320 psi

@Strain 5.21 %,
Temperature 356 °F
 DAM; ISO 11403-1 -2
79.62 MPa

@Strain 8.50 %,
Temperature 150 °C
 11550 psi

@Strain 8.50 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
82.36 MPa

@Strain 2.68 %,
Temperature 90.0 °C
 11950 psi

@Strain 2.68 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
83.34 MPa

@Strain 3.62 %,
Temperature 150 °C
 12090 psi

@Strain 3.62 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
84.28 MPa

@Strain 4.40 %,
Temperature 160 °C
 12220 psi

@Strain 4.40 %,
Temperature 320 °F
 DAM; ISO 11403-1 -2
84.82 MPa

@Strain 1.46 %,
Temperature 23.0 °C
 12300 psi

@Strain 1.46 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
91.22 MPa

@Strain 2.14 %,
Temperature 90.0 °C
 13230 psi

@Strain 2.14 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
96.18 MPa

@Strain 2.14 %,
Temperature 40.0 °C
 13950 psi

@Strain 2.14 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
99.59 MPa

@Strain 8.88 %,
Temperature 150 °C
 14440 psi

@Strain 8.88 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
102.17 MPa

@Strain 1.00 %,
Temperature 40.0 °C
 14819 psi

@Strain 1.00 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
105.9 MPa

@Strain 2.02 %,
Temperature 23.0 °C
 15360 psi

@Strain 2.02 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
109.3 MPa

@Strain 3.05 %,
Temperature 90.0 °C
 15850 psi

@Strain 3.05 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
113.89 MPa

@Strain 1.36 %,
Temperature 0.000 °C
 16518 psi

@Strain 1.36 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
131.27 MPa

@Strain 1.25 %,
Temperature -20.0 °C
 19039 psi

@Strain 1.25 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
138.45 MPa

@Strain 1.80 %,
Temperature 0.000 °C
 20081 psi

@Strain 1.80 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
139.51 MPa

@Strain 1.35 %,
Temperature 23.0 °C
 20234 psi

@Strain 1.35 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
141.94 MPa

@Strain 1.56 %,
Temperature 40.0 °C
 20587 psi

@Strain 1.56 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
148 MPa

@Strain 1.40 %,
Temperature 0.000 °C
 21500 psi

@Strain 1.40 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
157 MPa

@Strain 1.47 %,
Temperature -20.0 °C
 22800 psi

@Strain 1.47 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
160.61 MPa

@Strain 2.32 %,
Temperature 0.000 °C
 23295 psi

@Strain 2.32 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
162.51 MPa

@Strain 1.65 %,
Temperature -20.0 °C
 23570 psi

@Strain 1.65 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
167.15 MPa

@Strain 2.06 %,
Temperature 40.0 °C
 24243 psi

@Strain 2.06 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
175.14 MPa

@Strain 1.85 %,
Temperature 23.0 °C
 25402 psi

@Strain 1.85 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
187.61 MPa

@Strain 2.76 %,
Temperature 40.0 °C
 27211 psi

@Strain 2.76 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
188.82 MPa

@Strain 1.91 %,
Temperature 0.000 °C
 27386 psi

@Strain 1.91 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
199.51 MPa

@Strain 2.24 %,
Temperature -20.0 °C
 28937 psi

@Strain 2.24 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2