DSM Akulon® Ultraflow K-FHGM35 PA6-(GF+MD)40
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Akulon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Akulon® Ultraflow K-FHGM35 PA6-(GF+MD)40.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass Reinforced, Heat Stabilized, High Flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | dry; ISO 1183 |
| Water Absorption | 5.5 % | 5.5 % | Sim. To ISO 62 |
| Moisture Absorption | 1.70 % | 1.70 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | cond; ISO 527-1/-2 |
| 120 MPa | 17400 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| 5.0 % | 5.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | cond; ISO 527-1/-2 |
| 9.03 GPa | 1310 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 165 MPa | 23900 psi | dry; ISO 178 |
| Flexural Modulus | 7.72 GPa | 1120 ksi | dry; ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 3.49 J/cm² @Temperature 23.0 °C |
16.6 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 4.49 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.399 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 0.399 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA | |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 0.598 J/cm² @Temperature 23.0 °C |
2.85 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.9 µm/m-°C | 19.4 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | dry; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | cond; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
dry; IEC 60250 | |
| 4.5 @Frequency 1.00e+6 Hz |
4.5 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 14 @Frequency 100 Hz |
14 @Frequency 100 Hz |
cond; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | cond; IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | dry; IEC 60243-1 | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| 0.12 @Frequency 1.00e+6 Hz |
0.12 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 0.32 @Frequency 100 Hz |
0.32 @Frequency 100 Hz |
cond; IEC 60250 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ PC-000/15T-S2 NATURAL Polycarbonate (PC)
- Nilit Nilamid B3 H G8 40% Glass Fiber Reinforced PA6
- Parker Chomerics SOFT-SHIELD® 7000 Low Closure Force EMI Gasket
- H.C. Starck Amperit® 250.1 Water Atomized (NiCr 80-20)
- Karina 4000/35-IE MBPEBD Green Color Concentrate
- Total Lumicene® MR 2001 Polypropylene, Metallocene Polypropylene
- ChevronTexaco Rando® HDZ 15
- ExxonMobil LLDPE LL 1002YB Cast Linear Low Density Polyethylene Resin
- Chosun Refractories ASC-S Alumina Silicon Carbide Carbon Bricks for Torpedo Car
- Eurotec® Tecomid® NB40 GR30 NL IH PA 6 30% glass fiber reinforced, impact modified
Copyright © lookpolymers.com All Rights Reserved