Covestro Makrolon® DP 1-1456 Polycarbonate, Impact Grade

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer Covestro
Trade Name Makrolon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Makrolon® DP 1-1456 Polycarbonate, Impact Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impact modified injection molding grade, extremely easy flow and easy mold release, for thin walled applications with long flow lengths.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Water Absorption 0.35 %
0.35 %
Saturation in water
Moisture Absorption at Equilibrium 0.15 %
0.15 %
Equilibrium at 50% RH
Water Absorption at Saturation 0.35 %
0.35 %
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 27 g/10 min

@Load 1.20 kg,
Temperature 300 °C
27 g/10 min

@Load 2.65 lb,
Temperature 572 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
Elongation at Break >= 50 %
>= 50 %
Nominal
Elongation at Yield 5.5 %
5.5 %
Tensile Modulus 2.00 GPa
290 ksi
Flexural Yield Strength 83.0 MPa
12000 psi
at 5% strain; ASTM D790
Flexural Modulus 2.10 GPa
305 ksi
ASTM D790
Izod Impact, Notched 5.87 J/cm

@Thickness 3.20 mm
11.0 ft-lb/in

@Thickness 0.126 in
ASTM D256
Charpy Impact Unnotched NB
NB
Impact Test 65.0 J

@Thickness 3.20 mm
47.9 ft-lb

@Thickness 0.126 in
Instrumented total energy; 3.2 mm thick; 0.5 in. dart; 3 in. clamp; 15 mph; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Deflection Temperature at 1.8 MPa (264 psi) 123 °C
253 °F
Vicat Softening Point 144 °C
291 °F
UL RTI, Electrical 80.0 °C

@Thickness 1.50 mm
176 °F

@Thickness 0.0591 in
UL RTI, Mechanical with Impact 80.0 °C

@Thickness 1.50 mm
176 °F

@Thickness 0.0591 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.50 mm
176 °F

@Thickness 0.0591 in
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
(Black)
Processing Properties Metric English Comments
Melt Temperature 293 - 332 °C
559 - 630 °F