- A. Schulman POLYFORT™ FPP 1200X High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
A. Schulman POLYFORT™ FPP 1200X High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 1200X High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1200X is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Melt Flow | 30 g/10 min | 30 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ASTM D785 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Modulus | 2.618 GPa | 379.7 ksi | ASTM D790 |
| Izod Impact, Notched | 0.907 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IS7015 Unitape Unidirectional Polypropylene-Glass Composite
- Nilit Nilamid B3 H ZB Unfilled, Low Temperature Impact Resistant PA6
- Resinlab® CYNERGY CA6204 Adhesive
- Heatbath/Park High Speed 60 High Speed Hardening Salt
- SABIC Innovative Plastics NORYL GTX870 PPE+PA6 (Asia Pacific)
- Lubrizol Isoplast® 2540 Engineering Thermoplastic Polyurethane Resin for Medical Applications
- Zhejiang Juner 302-G30 30% Glass Fibre Reinforced, Flammable Resistant, and Low Separate Out Mode
- Dow TONE™ 0310 Polyol
- 3M Scotch-Weld™ 2158 B/A Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved