- Clariant Renol TPU2087AFR Polyurethane Elastomer, Flame Retardant
Clariant Renol TPU2087AFR Polyurethane Elastomer, Flame Retardant
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol TPU2087AFR Polyurethane Elastomer, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 84 | 84 | ASTM D2240 |
| Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D412 |
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-0 @Thickness 1.52 mm |
V-0 @Thickness 0.0600 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 210 °C | 380 - 410 °F | |
| Mold Temperature | 37.8 - 65.6 °C | 100 - 150 °F | |
| Dry Time | 2 - 4 hour @Temperature 104 °C |
2 - 4 hour @Temperature 220 °F |
to ensure moisture level is less than 0.02% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CH042V Polypropylene, Homopolymer, Extrusion, Sheet
- Overview of materials for Polyphthalamide (PPA), Stainless Fiber, EMI
- DuPont™ Clysar® HP Polyolefin Shrink Packaging Film, 100 Gauge (discontinued **)
- Karina E 36/234-FC-LMP Brown Color Concentrate for PVC
- Supreme Petrochem SP 266 Toughened Polystyrene
- A. Schulman POLYBATCH™ AO-25 Antioxidant Masterbatch Based in LDPE
- Zell-Metall Engineering Plastics Zellamid 1115
- DSM Arnitel® PM471 45 Shore D, Extrusion Grade Copolyester Elastomer (North America)
- BASF Pluracol® 3042 Specialty Polyol
Copyright © lookpolymers.com All Rights Reserved