- Samsung Cheil Industries Infino® GP-5400G PBT, 40% Glass Filled
Samsung Cheil Industries Infino® GP-5400G PBT, 40% Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GP-5400G PBT, 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Material with 40% GF reinforcement that is used in motor insulatorsInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 137 MPa | 19900 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 206 MPa | 29900 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.08 GPa | 156 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.932 J/cm @Thickness 3.17 mm |
1.74 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.750 - 3.00 mm |
HB @Thickness 0.0295 - 0.118 in |
Users viewing this material also viewed the following:
- PSM Industries Ferro-TiC® CS-40 Martensitic Stainless Steel
- Sumitomo Bakelite Durez® 22257 Phenolic, Compression Grade
- Diamond Polymers ABSPC 7030-HES ABS/PC Injection Molding Grade, High Impact
- ConocoPhillips Conoco® El Mar® Ashless Heavy Duty Oil, SAE Viscosity Grade 30
- BASF Ultramid® 7523-2AM BK ND3007 33% Glass Filled PA66 (Dry)
- BASF Ultramid® C40 01 PA66/6 (Dry)
- Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 10% Plasticizer (discontinued **)
- BASF Luranyl® KR 2456/3 Polyphenylene Ether + Styrene-Butadiene Blend
Copyright © lookpolymers.com All Rights Reserved