Clariant Renol PA113G13X050 Nylon 66, 13% Glass Fiber, Heat Stabilized, Lubricated, Improved Ductility
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled , Nylon 66, Heat Stabilized |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA113G13X050 Nylon 66, 13% Glass Fiber, Heat Stabilized, Lubricated, Improved Ductility.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 4.34 GPa | 630 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Temperature 22.8 °C |
1.60 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- RheTech Products FT3080-729UV Thermoplastic Polyolefin, UV Stabilized, AG-64 Grey
- PTS Trimid® N66-G33HL 33% Glass Fiber Reinforced Heat Stabilized, Lubed Nylon 6/6
- Chevron Phillips Marlex® C579 High density polyethylene (discontinued **)
- Styrolution Terluran® GP-22 ABS
- SABIC Innovative Plastics NORYL NH5120C PPE+PS (Asia Pacific)
- Teknor Apex Sinpolene MBW108LE Low Density Polyethylene
- Toyobo PELPRENE™ S2002FB Polyester TPE, Flame Resistant
- Zoltek Panex 35® Uni-Directional Carbon Fiber Prepreg
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR DBPH-50
- DuPont Performance Polymers Zytel® HTN FR52G20NH NC010 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved