Clariant Renol 6004G23 Nylon 6, 23% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol 6004G23 Nylon 6, 23% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Filler Content | 23 % | 23 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 121 MPa | 17500 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 165 MPa | 24000 psi | ASTM D790 |
| Flexural Modulus | 5.58 GPa | 810 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Temperature 22.8 °C |
3.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 260 °C | 460 - 500 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Matrixx Group 80S7351 35% Glass Reinforced PET (discontinued **)
- Kraton® D1192 A (SBS) Liner Block Copolymer
- SABIC Innovative Plastics LNP STAT-KON SE002Z PA 12 (Asia Pacific)
- Toho Tenax Besfight® G30-400 1K HTA-7W EP01 Continuous Filament Carbon Fiber
- Total PPC 10642 Polypropylene, Heterophasic Copolymer, Injection Molding
- DuPont Elvanol® 70-27 Polyvinyl Alcohol Intermediately Hydrolyzed General Purpose Grade
- DuPont Performance Polymers Zytel® 70G35HSLX BK357 Nylon 66 (Unverified Data**)
- Alliance Polymers Zythane™ 5050D Thermoplastic Polyurethane Elastomer
- Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.35 g/cc Green Density
- Ashley Polymers Ashlene® 827B Nylon 6
Copyright © lookpolymers.com All Rights Reserved