Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Stainless Steel Fiber |
Manufacturer | Clariant |
Trade Name | |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Clariant PCSP0014 GREY Polycarbonate, Stainless Steel Fiber, EMI.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
Flexural Yield Strength | 103 MPa | 15000 psi | ASTM D790 |
Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 135 - 152 °C | 275 - 305 °F | |
Mold Temperature | 35.0 - 48.9 °C | 95.0 - 120 °F | |
Dry Time | 2 - 4 hour @Temperature 48.9 °C |
2 - 4 hour @Temperature 120 °F |
to eliminate surface defects |
Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
Shot Size | 30 - 80 % | 30 - 80 % | |
Screw Speed | 20 - 100 rpm | 20 - 100 rpm |