- Clariant PA123G20 Nylon 66, 20% Glass Fiber, Impact Modified, Heat Stabilized
Clariant PA123G20 Nylon 66, 20% Glass Fiber, Impact Modified, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Heat Stabilized |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant PA123G20 Nylon 66, 20% Glass Fiber, Impact Modified, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Yield Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 440 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GA-1046HLF PVC Compound
- Palm Labs Adhesives Turbo Fuse Series 130SI Surface Insensitive (100 Viscosity) Rapid Bonding Adhesive
- Sibur DST-30-01 2nd Group Styrene-Butadiene-Styrene Block Copolymer (SBS-TPE)
- Goodfellow Ruby, Al2O3
- DuPont Performance Polymers Kalrez® Spectrum™ 7090 Fluoroelastomer
- China-Yixing Longly Refractories ZTA (20%ZrO2) Zirconia Toughened Alumina Composite Ceramic
- BASF DEA Diethylamine anhydrous
- BASF Lupranate® M20SB Isocyanate
- PlastxWorld Veroplas PA2002HI Nylon 6
Copyright © lookpolymers.com All Rights Reserved