Westlake Mxsten CV77515 Polyethylene Plastomer

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Westlake Chemical Corporation
Trade Name Mxsten
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Westlake Mxsten CV77515 Polyethylene Plastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Mxsten CV Plastomer CV77515 resin is a polyethylene plastomer designed for blown film extrusion and food packaging that contains 1,000 ppm slip and no antiblock additives. Films produced with this resin exhibit a very low seal initiation temperature with a broad hot tack window. Other features of this resin include higher stiffness and high melting point. This resin grade complies with 21 CFR 177.1520. Blown film processing temperatures of 420� F � 450� F are recommended for Westlake Chemical CV77515. Gauge of test specimens 1.0 mil fabricated on a 6" die, 2.5" 24:1 L:D barrier screw, 2.4:1 BUR, 100-mil die gap, 15" frostline height, 450� F melt temperature, and 7.5 lb/hr/inch die output. Density results are on Base Resin.
Physical Properties Metric English Comments
Density 0.910 g/cc
0.0329 lb/in³
ASTM-D4883
Thickness 25.4 microns
1.00 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 750 %
750 %
ASTM-D822
Film Elongation at Break, TD 1050 %
1050 %
ASTM-D822
Dart Drop 66.9 g/micron
1700 g/mil
ASTM-D1709A
Dart Drop Test 1700 g
3.75 lb
ASTM-D1709A
Film Tensile Strength at Break, MD 56.0 MPa
8120 psi
ASTM-D882
Film Tensile Strength at Break, TD 44.0 MPa
6380 psi
ASTM-D882
Heat Seal Strength Initiation Temperature 88.0 °C
190 °F
Temperature at which 200 g/in. seal strength is achieved.; Westlake Test
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM-D1003
Gloss 60 %
60 %
Angle 45°; ASTM-D2457
Descriptive Properties Value Comments
Process Blown Film