| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant CA9000NAT` Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.022 cm/cm | 0.022 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 |
| Flexural Yield Strength | 97.9 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C |
1.30 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 160 - 182 °C | 320 - 360 °F | |
| Middle Barrel Temperature | 166 - 193 °C | 330 - 380 °F | |
| Front Barrel Temperature | 171 - 204 °C | 340 - 400 °F | |
| Nozzle Temperature | 177 - 210 °C | 350 - 410 °F | |
| Melt Temperature | 191 - 204 °C | 375 - 400 °F | |
| Mold Temperature | 65.6 - 79.4 °C | 150 - 175 °F | |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
Users viewing this material also viewed the following:
- MV Labs Y100 Y(C2H3O2)3·4H2O Yttrium acetate hydrate
- Quadrant EPP TIVAR® CleanStat™ FDA, USDA, 3-A Dairy, Electro Static Dissipative UHMW-PE (ASTM Product Data Sheet)
- Master Bond EP33CLV Epoxy Resists Chemicals and High Temperatures
- Lubrizol Estaloc® 61225 Polyester-Type Thermoplastic Alloy
- Chosun Refractories RSP-M Blast Furnace Runner Refractory
- Eurostar Starpylen MX06050 PP, 30% Glass Filled, Injection Molded
- Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (1.5 mm Molded Thickness)
- BASF Procom® D 1026 Polypropylene
- DuPont Performance Polymers Hytrel® 3078 TPC-ET (Unverified Data**)
- Termopol Termoton® K2GA2060A TPE Compound, based on SEBS and Polyolefins
Copyright © lookpolymers.com All Rights Reserved