Clariant 6004G8-HSL BK UV Black Nylon 6, 8% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant 6004G8-HSL BK UV Black Nylon 6, 8% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Filler Content | 13 % | 13 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C |
1.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Middle Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Front Barrel Temperature | 254 - 271 °C | 490 - 520 °F | |
| Nozzle Temperature | 254 - 274 °C | 490 - 525 °F | |
| Melt Temperature | 254 - 271 °C | 490 - 520 °F | |
| Mold Temperature | 79.4 - 121 °C | 175 - 250 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content of 0.2% or less |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 1500H (S30G) Propylene Homopolymer
- ExxonMobil Santoprene® 241-80 Thermoplastic Elastomer (discontinued **)
- Dow Questra® WA552 High Heat Syndiotactic Polystyrene, 30% Glass Filled (discontinued **)
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer (discontinued **)
- Karina 550D35/1-AT-IS Ivory PVC Compound
- ExxonMobil 220 Mobil DTE PM Ashless
- DuPont Performance Polymers Zytel® 73G30T BK261 Nylon 6 (Unverified Data**)
- ChevronTexaco Vistac® ISO 150 Rock Drill Oil
- Fainplast Compounds PG 58/1AT Flexible PVC, Extrusion Modified with Rubber
- 3M Dyneon™ FC 5157 Elastomer Additive
Copyright © lookpolymers.com All Rights Reserved