Chi Mei Polylac® PA-756H ABS - High Flow
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-756H ABS - High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Super high flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Melt Flow | 75 g/10 min @Load 10.0 kg, Temperature 220 °C |
75 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 107 MPa | 15500 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| Impact | 8.00 | 8.00 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | unannealed; ISO 75 |
| 97.0 °C | 207 °F | annealed; ISO 75 | |
| Vicat Softening Point | 95.0 °C @Load 5.00 kg |
203 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 102 °C @Load 1.00 kg |
216 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 104 °C @Load 1.00 kg |
219 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- H.C. Starck Amperit® 161.065 Niobium (Nb)
- Techmer ES HiFill® PA4/6 GF45 HS BK 45% Glass Filled
- Star Plastics PC743 Molding Grade PC
- Suqian Unitechem Hindered Amine Light Stabilizer 770
- Zeon Chemicals Nipol® 33-5SR Nitrile Elastomer
- Hexcel® HexForce™ 4527 Fiber Glass Fabric
- Aclo Accutech Polypropylene Homopolymer HP0339G10M20CL Glass/Mineral Reinforced Coupled
- Arkema Group Evatane® 1005 VN 2 Ethylene Vinyl Acetate
- Resinlab® CYNERGY CA6904 Adhesive
Copyright © lookpolymers.com All Rights Reserved