- Chi Mei Kibisan® PN-117 SAN
Chi Mei Kibisan® PN-117 SAN
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Kibisan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Kibisan® PN-117 SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Melt Flow | 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 14 g/10 min @Load 3.80 kg, Temperature 230 °C |
14 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 | |
| 32 g/10 min @Load 10.0 kg, Temperature 220 °C |
32 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 83 | 83 | ASTM D790 |
| Ball Indentation Hardness | 159 MPa | 23100 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
| 69.36 MPa @Thickness 3.17 mm |
10060 psi @Thickness 0.125 in |
ASTM D638 | |
| Elongation at Break | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 97.9 MPa @Thickness 3.17 mm |
14200 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 0.166 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.310 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 |
| 0.176 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.330 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 |
| Impact | 3.00 | 3.00 | Impact Flexural Test Notched (KJ/m²) |
| 19.0 | 19.0 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | unannealed; ISO 75 |
| 97.0 °C | 207 °F | annealed; ISO 75 | |
| Vicat Softening Point | 102 °C @Load 5.00 kg |
216 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 104 °C @Load 5.00 kg |
219 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 106 °C @Load 1.00 kg |
223 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 109 °C @Load 1.00 kg |
228 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Lavergne VYTEEN PC/ABS 8515 Polycarbonate - Acrylonitrile Butadiene Styrene Alloy
- Teknor Apex Monprene® MP-2228C Thermoplastic Elastomer
- Hexcel® Redux® 609 (0.06 psf) Adhesive film for bonding metallic and composite components
- A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene
- DSM Akulon® F130-E1 PA6
- Ensinger TECANYL™ MT Autoclavable Polymer
- Fainplast Compounds PH 74/AL Flexible PVC, Transparent Extrusion
- Arkema Group Lucalor® PEY 221 CPVC, Pipe Grade
- ExxonMobil CM-L Mobilgrease CM Series
Copyright © lookpolymers.com All Rights Reserved