CP-Polymer-Technik Wellamid® 6000/42 CP Nylon 6, Polymer Modified, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000/42 CP Nylon 6, Polymer Modified, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.5 - 3.3 % | 2.5 - 3.3 % | 23°C/50%RH; DIN 53495 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm @Thickness 4.00 mm |
0.0080 - 0.012 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527 |
| Flexural Modulus | 1.90 GPa | 276 ksi | DIN 52457 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| Melting Point | 215 °C | 419 °F | Kofler |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 179 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 179 |
| Vicat Softening Point | 170 °C | 338 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Stufe; IEC 707 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Stufe; IEC 707 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ISO 3915 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.020 | 0.020 | At 1 MHz; IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | Stufe; IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | Medium | |
| Screw Speed | Medium |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 50 LS PA66, 50% glass fibre, light stability
- Quadrant EPP Quadrant Nylon 101 Extruded, Unfilled, Type 66 Natural and Black (ASTM Product Data Sheet)
- Iran Petrochemical (PCC) EPD 60 R Polypropylene
- LATI Latilub 66-15T K/30 PA66, 30% Carbon Fiber Reinforced, PTFE Filled
- Chevron Phillips K-Resin® KR05NW Styrene-Butadiene Copolymer, Sheet and Blow Mold Grade
- ExxonMobil Exxtral™ BNU 013 Performance Polyolefin
- Bohler-Uddeholm BÖHLER S590 MICROCLEAN® High Speed Steel
- Bulk Molding Compounds BMC SLC 1000 Glass Reinforced Polyester
Copyright © lookpolymers.com All Rights Reserved