SABIC Innovative Plastics LNP THERMOCOMP DF006P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF006P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF006P is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| 1.424 g/cc | 0.05145 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00090 cm/cm @Time 86400 sec |
0.00090 in/in @Time 24.0 hour |
ISO 294 |
| 0.0015 cm/cm @Time 86400 sec |
0.0015 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0051 cm/cm @Time 86400 sec |
0.0051 in/in @Time 24.0 hour |
ISO 294 |
| 0.0067 cm/cm @Time 86400 sec |
0.0067 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 124 MPa | 18000 psi | Type I, 5 mm/min; ASTM D638 |
| 125 MPa | 18100 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 124 MPa | 18000 psi | Type I, 5 mm/min; ASTM D638 |
| 125 MPa | 18100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 10.01 GPa | 1452 ksi | 1 mm/min; ISO 527 |
| 10.48 GPa | 1520 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.72 GPa | 1260 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.74 J/cm | 14.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² | 22.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C @Thickness 3.20 mm |
273 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- PolyChem Alloy 5004 Talc Nucleator
- Ovation Polymers OpteSTAT™ NC PK 8010 Polyetheretherketone based Carbon Nanotube Compound
- Shin-Etsu Silicones KF-9901 Fluid
- A. Schulman POLYBATCH™ Orange LL10257/4 Concentrate Based In LLDPE
- A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 3.0 PHR MBTS
- A. Schulman PP 2173-01 Polypropylene High-Impact Polypropylene
- Covestro Desmopan® 786 Thermoplastic Polyurethane
- 3M Controltac™ IJ3552C Changeable Graphic Film with Comply™ Adhesive
- GEHR Plastics Noryl PPO-30 GF 30% Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved