CENTROPLAST CENTROMID 6.6 FG Polyamide 6.6, Food Grade
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | CENTROPLAST Engineering Plastics GMBH |
| Trade Name | CENTROMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CENTROPLAST CENTROMID 6.6 FG Polyamide 6.6, Food Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This material has good hardness, wear resistance, abrasion strength and impact strength.Information provided by CENTROPLAST Engineering Plastics GMBH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | in normal climate 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 8.0 % | 8.0 % | in water at 23°C; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 @Thickness 10.0 mm |
88 @Thickness 0.394 in |
ISO 2039-2 |
| Ball Indentation Hardness | 160 MPa | 23200 psi | value at 30 sec.; ISO 2039-1 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | v = 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 40 % | >= 40 % | ISO 527-2 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527-2 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | |
| Melting Point | 260 °C | 500 °F | 10K/min; ISO 3146 |
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Long Term |
| 180 °C | 356 °F | Short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F | |
| Flammability, UL94 | V-2 @Thickness 1.00 mm |
V-2 @Thickness 0.0394 in |
|
| V-2 @Thickness 6.00 mm |
V-2 @Thickness 0.236 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
IEC 60250 |
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | in transformer oil; IEC 60243-1 |
| Dissipation Factor | 0.013 @Frequency 100 Hz |
0.013 @Frequency 100 Hz |
IEC 60250 |
| 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Food Compliance | yes | BGVV |
| yes | FD A |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® S3000-S3N Silver-Coated Solid Glass Spheres
- Palm Labs Adhesives TURBO SEAL SERIES 55 BROWN FINE THREADS THREAD SEALANT
- SABIC Innovative Plastics Lexan® 500R PC (Asia Pacific)
- Momentive Performance Materials TSE3940 Gray Adhesive Sealant, Fast Cure Paste
- Shin-Etsu Silicones KMP-590 Fluid
- Shuman 720H Black ABS
- A. Schulman FORMION™ FI 226 40% Glass Fiber Reinforced Ionomer / Nylon Alloy
- ChevronTexaco Capella® HFC Auto
- ExxonMobil HDPE HYA 600 High Density Polyethylene Resin
- Dow Corning 2-1865 Microemulsion
Copyright © lookpolymers.com All Rights Reserved